IMPACT – RESISTANT APPLICATION

MF1-GF-300-P
280-325 HB
C: 0.1     Si: 0.5 
Mn:2       Cr:1,5       
Mo:0,4
Low alloyed tubular wire for building up applications that can be used for multi-layer welding, because the deposit is ductile and free of cracks.

MF3-GF-45-PT

42-45 HRC
C: 0.2    Cr:4.5       
Mo: 3      V: 0.2
For hardfacings of approx. 450HB hardness. Weld metal is machinable with carbide tools and can be used for multi-layer welding..

MF6-GF-55-RP

56-57 HRC
C: 0.5 Si: 2,7
Cr: 9.5
Wire electrodes for impact-and abrasion-resistant hardfacings of prox.600HB. Deposits are hard and tough. For difficult base materials, preheating or a buffer layer with F-250 is recomended.

MF6-GF-55-PT

54-56 HRC
C: 0.5 Si: 1
Mn: 3 Cr:6,5

Mo: 0,8 V: 0,4

MF6-GF-60-PT

55-58 HRC
C: 0.5 Si: 1
Mn: 3 Cr:6
Mo: 1,6 V: 0,4
W:1
Deposit with excellent resistance to abrasion and impact creep resistant up to 550°C. Deposit can be heat treated to increase hardness. For bulldozer teeth, crusher jaws,baffles, coal planes and drill pipes.

MF6-GF-60-GP

56-58 HRC
C: 1.8 Si: 14
Cr: 7
Mo:1,4 Ti: 5
For parts which are exposed to high abrasive wear in combination with impact stress. The deposit is martensitic with included titanium carbides. Application are cement crusher rolls, pulveriser rolls and hammers.